• Temperature maximum is 60℃ (140℉).
• Refrigeration will increase shelf life but a warm
　 up period of1 hour is then required before use.

  To apply, place "press" portion of tab on SEM
  mount surface, lift "Lift Off" tab and peel.
• Can be cut to size as desired.

• Thickness：0.16mm；Can used dowm：-20℃.
• It may be used for scanning electron microscopy
  or EDS applications.

• Average flake size：1 μm.
• Service temperature：200℃.

• Should be mixed or spatulated well before using.
• Specific Gravity：2.25 gm/cc.
• Viscosity：445 poise.

• Particle size：0.4-1.0μm,80% are below 1.0μm.
• Cures in 16-50 hours or in 30 minutes at 125-150℃.

• Core diameter of this aluminum roll：76mm.
• Foil Thickness：0.05 mm.
• Total Thickness (foil+adhesive)：0.081mm.
• Electrical Resistance adhesive：0.010 ohm.

• The core diameter：76mm
• Foil Thickness：0.04 mm
• Total Thickness：0.07 mm
• Resistance through adhesive：0.010 ohm

• The type is dead soft copper with a conductive acrylic   adhesive

• Nickel is embedded in the adhesive
• Overall thickness：0.075mm
• Adhesive：0.040mm
• Conductive resistivity is 0.004 ohm/square

• A unique feature of thisios the red color that
  appears on curing.
• It has good adhesive to many materials
  including metals, ceramics, glass and most
  plastics.

• It has low viscosity and is extremely thin, with
  minimum creep, hystersis and linearity problems.
• Operating temperature range, short term is
　-269° to +370℃；long term, -269° to +260℃.
• Elongation can occur at +24℃ (3%).

• Vibratome, Microslicer applications and other
  quick-set tissue-slide uses.